PA6 Modification

Raw Materials Modified Nylon

PA6 GF15 NC

Home > Products > Modified Nylon > PA6 Modification
Labels : PA6+15% glass fiber reinforcement, high fluidity, high surface quality.
InquiryInquiry
  • Self-adhesive Tie Mounts 1-1
Product Description
Overview

◆ Material : PA6+15% glass fiber reinforcement, high fluidity, high surface quality.

◆ Characteristics : PA6 reinforced material, which exhibits excellent mechanical properties and good flowability.

◆ Purpose : automotive parts, electronic and electrical products, mechanical components, engineering accessories, etc.

◆ Benchmark Against : BASF B3EG3, DUPONT (CELANES) 73G15L

Technical Parameters
项 目
Item		 测试标准
Standard		 测试条件
Condition		 单 位
Unit		 数 值
Value
Density ISO 1183 23℃/55%RH g/cm3 1.23
Filler Contents ISO 3451 800℃/2H % 15
Tensile Strength ISO 527-2 5mm/min Mpa 130
Elongation at Break ISO 527-2 5mm/min % 3.8
Tensile Modulus ISO 527-2 5mm/min Mpa 6000
Flexural Strength ISO 178 2mm/min Mpa 180
Flexural Modulus ISO 178 2mm/min Mpa 4500
Izod Notched Impact Strength ISO 180/1A 2.75J KJ/ M2 8
Izod Unnotched Impact Strength ISO 180/1U 5.5J KJ/ M2 45
Flammability UL-94 - class HB
Melt Point ISO 11357 - ℃ 222

Previous : Back to List

Next : PA6 GF10 R01