◆ Material : PA66+33% GF belongs to glass fiber reinforced PA66, containing 33% glass fiber additives, with a granular appearance and processing grade of injection molding.
◆ Characteristics : High strength, high rigidity, heat resistance, dimensional stability, low friction, easy demolding, suitable for high temperature and high load structural components.
◆ Purpose : Widely used in the automotive industry, such as cooling fans, door handles, etc; In the field of electronic appliances, such as connectors, wire spools, etc; And industrial components such as chair seats, pulleys, etc.
◆ Benchmark Against : DUPONT 70G33L
| 项 目 Item |
数 值 Value |
单 位 Unit |
测试标准 Standard |
测试条件 Condition |
| Density | 1.39 | g/cm3 | ISO 1183 | 23℃/55%RH |
| Filler Contents | 33 | % | ISO 3451 | 800℃/2H |
| Tensile Strength | 200 | Mpa | ISO 527-2 | 5mm/min |
| Elongation at Break | 3.0 | % | ISO 527-2 | 5mm/min |
| Tensile Modulus | 11000 | Mpa | ISO 527-2 | 5mm/min |
| Flexural Strength | 262 | Mpa | ISO 178 | 2mm/min |
| Flexural Modulus | 9300 | Mpa | ISO 178 | 2mm/min |
| Charpy impact strength | 13 | KJ/ M2 | ISO 180/1A | 2.75J |
| Charpy Unnotched impact strength | 80 | KJ/ M2 | ISO 180/1U | 5.5J |
| Flammability | HB | class | UL-94 | - |
| Melt Point | 260 | ℃ | ISO 11357 | - |
* If you need the material PA66+33%GF or require customized production with special specifications, you can contact us at email sales@anixt.com ,We will reply promptly!