◆ PA1010 Type III Material : Support the further optimization of its strength, rigidity, or conductivity by adding modifications such as glass fiber and carbon fiber, to meet the customized needs of specific scenarios.
◆ PA1010 Type III Characteristics : It maintains structural stability even in high-temperature environments, balancing lightweight and strength requirements. It is resistant to fracture when subjected to external forces and possesses good toughness.
◆ PA1010 Type III Purpose : Applied to the extrusion of nylon tubing, including oil hoses, air hoses, etc.
◆ PA1010 Type III Benchmark Against : -
| 项 目 Item |
数 值 Value |
单 位 Unit |
测试标准 Standard |
测试条件 Condition |
| Density | 1.05 | g/cm3 | ISO 1183 | 23℃/55%RH |
| Filler Contents | - | % | ISO 3451 | 800℃/2H |
| Tensile Strength | 55 | Mpa | ISO 527-2 | 5mm/min |
| Elongation at Break | 210 | % | ISO 527-2 | 5mm/min |
| Tensile Modulus | - | Mpa | ISO 527-2 | 5mm/min |
| Flexural Strength | ≥20 | Mpa | ISO 178 | 2mm/min |
| Flexural Modulus | 1500 | Mpa | ISO 178 | 2mm/min |
| Charpy impact strength | 6 | KJ/ M2 | ISO 180/1A | 2.75J |
| Charpy Unnotched impact strength | N | KJ/ M2 | ISO 180/1U | 5.5J |
| Flammability | HB | class | UL-94 | - |
| Melt Point | 190 | ℃ | ISO 11357 | - |
* If you need the material PA1010 Type III or require customized production with special specifications, you can contact us at email sales@anixt.com ,We will reply promptly!