◆ PA1010 Type II Material : With excellent mechanical properties, chemical resistance, wear resistance, and self-lubricating properties, it has been widely used in automotive, electronics, machinery manufacturing, and other fields.
◆ PA1010 Type II Characteristics : It features low water absorption, good dimensional stability, excellent wear resistance, and self-lubricating properties; it can be used under light load, low temperature, high humidity fluctuation, and with no or minimal lubrication.
◆ PA1010 Type II Purpose : In the automotive industry, it is used to manufacture fuel system components; in the electronics field, it is commonly used in connectors and switches; and in the medical field, it is used in surgical instrument handles and other components with high hygiene requirements.
◆ PA1010 Type II Benchmark Against : -
| 项 目 Item |
数 值 Value |
单 位 Unit |
测试标准 Standard |
测试条件 Condition |
| Density | 1.04 | g/cm3 | ISO 1183 | 23℃/55%RH |
| Filler Contents | - | % | ISO 3451 | 800℃/2H |
| Tensile Strength | ≥50 | Mpa | ISO 527-2 | 5mm/min |
| Elongation at Break | ≥260 | % | ISO 527-2 | 5mm/min |
| Tensile Modulus | - | Mpa | ISO 527-2 | 5mm/min |
| Flexural Strength | ≥75 | Mpa | ISO 178 | 2mm/min |
| Flexural Modulus | 1600 | Mpa | ISO 178 | 2mm/min |
| Charpy impact strength | 8.1 | KJ/ M2 | ISO 180/1A | 2.75J |
| Charpy Unnotched impact strength | N | KJ/ M2 | ISO 180/1U | 5.5J |
| Flammability | HB | class | UL-94 | - |
| Melt Point | 202 | ℃ | ISO 11357 | - |
* If you need the material PA1010 Type II or require customized production with special specifications, you can contact us at email sales@anixt.com ,We will reply promptly!