Brand : Anixt® PA6 GF20
Labels : PA6 filled with 20% glass fiber reinforcement features excellent mechanical properties and good fluidity.
Tags: PA6GF20 DUPONT73G20L
InquiryInquiry
  • PA6 GF20
Product Description
Overview

◆ Material : PA6 filled with 20% glass fiber reinforcement features excellent mechanical properties and good fluidity.

◆ Characteristics : Significant rigidity improvement: With 20% glass fiber content, its flexural modulus is approximately 8% higher than that of 73G15L with 15% glass fiber, delivering stronger deformation resistance.

◆ Purpose : Auto parts, electronic and electrical appliances, engineering accessories, etc.

◆ Benchmark Against : DUPONT 73G20L

Technical Parameters
项 目
Item		 数 值
Value		 单 位
Unit		 测试标准
Standard		 测试条件
Condition
Density 1.27 g/cm3 ISO 1183 23℃/55%RH
Filler Contents 20 % ISO 3451 800℃/2H
Tensile Strength 150 Mpa ISO 527-2 5mm/min
Elongation at Break 4.0 % ISO 527-2 5mm/min
Tensile Modulus 6500 Mpa ISO 527-2 5mm/min
Flexural Strength 210 Mpa ISO 178 2mm/min
Flexural Modulus 5500 Mpa ISO 178 2mm/min
Charpy impact strength 11 KJ/ M2 ISO 180/1A 2.75J
Charpy Unnotched impact strength 60 KJ/ M2 ISO 180/1U 5.5J
Flammability HB class UL-94 -
Melt Point 220 ℃ ISO 11357 -