Polyamide 612 - Nylon 612 - PA 612
PA612 Molecular Formula:NH(CH2)6CONH(CH2)10CO]n
PA612 Features:Compare with the PA610,the nylon 612 is smaller density, has low water absorption,better transparency,higher toughness and strength,better abrasion resistance,low molding shrinkage rate,better molding processability and dimensional stability,excellent chemical resistance.
PA612 Application:
It is mainly used for modification of the base material, also used as the toothbrush's bristlelike monofilament, monofilament, cable covering,electrical insulators and precision parts,etc.And it is used in the production of the injection molding products and injection products,according to the customer’s requirements.
PA610 Index:
| Test Items | UNIT | Standard Parameter Value | |
| Type I | TypeII | ||
| Viscosity Number | g/ml | 110±15 | 180±20 |
| Loss on Drying | ‰ | ≤1.0 | |
| Tensile Strength | MPa | ≥52 | |
| Elongation At Break | ％ | ≥160 | |
| Bending Strength | MPa | ≥60 | |
| Melting Point | ℃ | 230-280 | |
| Relative Density | G/cm3 | 1.06-1.08 | |
| Test Items | UNIT | PA612 Resin | ||
| A5G6301 | A5G7301 | A5RG7301 | ||
| Tensile Strength | MPa | 140 | 145 | 108 |
| Elongation At Break | % | 5 | 4 | 7 |
| Charpy Notch Impact | KJ/m2 | 15 | 12 | 35 |
| Charpy Non-Notch Impact | KJ/m2 | 85 | 75 | 100 |
| Flexural Strength | MPa | 200 | 202 | 150 |
| Flexural Module | MPa | 6600 | 7600 | 5400 |
| Ash Content | % | 30 | 35 | 35 |
* Note: