PA610 is used to make high impact strength and high toughness bushings.
r6wTransparent nylon-Transparent nylon_PA610_PA612_PA1010_PA121
PA610 is used to make corrosion-resistant valves, insulating devices, etc. in the chemical industry;
r6wTransparent nylon-Transparent nylon_PA610_PA612_PA1010_PA121PA610 is used to make precision electrical connectors, high-strength shells, high-temperature contactors, etc. in the electrical and electronic industry;
r6wTransparent nylon-Transparent nylon_PA610_PA612_PA1010_PA121PA610 is used in the electrical industry to make motor parts, terminals and switches that are used in harsh environments;
r6wTransparent nylon-Transparent nylon_PA610_PA612_PA1010_PA121PA610 is used in the production of high temperature resistant, high dimensional bushings and piston rings in the machinery industry.
r6wTransparent nylon-Transparent nylon_PA610_PA612_PA1010_PA121
| NO. |
ITEM |
TEST METHODS |
TEST CONDITION |
UNIT |
Typical value |
| CL6514-5 |
| Physical Propertids |
| 1 |
Density |
GB/T1033 |
23ºC |
-- |
1.08 |
| ISO1183 |
| 2 |
Molding shrinkage |
GB/T 15585 |
‐ |
% |
1.2 |
| 3 |
Shore hardness |
GB/T2411 |
‐ |
D |
84 |
| ISO2039 |
| 4 |
Melting point |
GB/T 4608 |
‐ |
ºC |
215 |
| ISO3146 |
| Mechanical Propertie |
| 5 |
Tensile strength |
GB/T 1040 |
50mm/min |
- |
≥59 |
| ISO527 |
| 6 |
Flexural strength |
GB 9341 |
2mm/min |
Mpa |
≥80 |
| ISO178 |
| 7 |
Flexural Module |
GB /T9341 |
2mm/min |
Mpa |
2100 |
| ISO178 |
| Remark |
|