PA612 Modification

Raw Materials Modified Nylon

PA612 157HSL

Home > Products > Modified Nylon > PA612 Modification
Labels : PA612 resin, with high fluidity, low water absorption, heat resistance and aging resistance.
InquiryInquiry
  • Self-adhesive Tie Mounts 1-1
Product Description
Overview

◆ Material : PA612 resin, with high fluidity, low water absorption, heat resistance and aging resistance.

◆ Characteristics : PA612 resin, this material possesses excellent properties such as impact strength, heat aging resistance, wear resistance, and low water absorption.

◆ Purpose : Cable ties, industrial accessories, automotive accessories, electronic accessories, etc.

◆ Benchmark Against : DUPONT (Celanese)157HSL

Technical Parameters
项 目
Item		 测试标准
Standard		 测试条件
Condition		 单 位
Unit		 数 值
Value
Density ISO 1183 23℃/55%RH g/cm3 1.08
Filler Contents ISO 3451 800℃/2H % -
Tensile Strength ISO 527-2 5mm/min Mpa 65
Elongation at Break ISO 527-2 5mm/min % 18
Tensile Modulus ISO 527-2 5mm/min Mpa 2500
Flexural Strength ISO 178 2mm/min Mpa 80
Flexural Modulus ISO 178 2mm/min Mpa 2300
Izod Notched Impact Strength ISO 180/1A 2.75J KJ/ M2 5
Izod Unnotched Impact Strength ISO 180/1U 5.5J KJ/ M2 NB
Flammability UL-94 - class HB
Melt Point ISO 11357 - ℃ 218