◆ Material : PA66 resin, high fluidity, easy demolding.
◆ Characteristics : PA66 resin, which possesses good toughness and excellent fluidity.
◆ Purpose : Sports equipment, industrial parts, automotive parts, etc.Typical applications include fast processing high stress technical parts or electrically insulating parts.
◆ Benchmark Against : Dupont (Celanese) 101L,BASF A3K
Technical Parameters
| 项 目 Item |
数 值 Value |
单 位 Unit |
测试标准 Standard |
测试条件 Condition |
| Density | 1.14 | g/cm3 | ISO 1183 | 23℃/55%RH |
| Filler Contents | - | % | ISO 3451 | 800℃/2H |
| Tensile Strength | 75 | Mpa | ISO 527-2 | 5mm/min |
| Elongation at Break | 10 | % | ISO 527-2 | 5mm/min |
| Tensile Modulus | 2800 | Mpa | ISO 527-2 | 5mm/min |
| Flexural Strength | 100 | Mpa | ISO 178 | 2mm/min |
| Flexural Modulus | 2500 | Mpa | ISO 178 | 2mm/min |
| Charpy impact strength | 6 | KJ/ M2 | ISO 180/1A | 2.75J |
| Charpy Unnotched impact strength | NB | KJ/ M2 | ISO 180/1U | 5.5J |
| Flammability | HB | class | UL-94 | - |
| Melt Point | 260 | ℃ | ISO 11357 | - |
* If you need the material PA66 101L or require customized production with special specifications, you can contact us at email sales@anixt.com ,We will reply promptly!