PA6 Modification

Raw Materials Modified Nylon

PA6 GF30 HSLR

Home > Products > Modified Nylon > PA6 Modification
Brand : Anixt® PA6 GF30 HSLR
Labels : PA6 reinforced with 30% glass fiber, featuring excellent surface finish, high mechanical strength and hydrolysis resistance.
Tags: PA6GF30HSLR
InquiryInquiry
  • PA6 GF30 HSLR
Product Description
Overview

◆ Material : PA6 reinforced with 30% glass fiber, featuring excellent surface finish, high mechanical strength and hydrolysis resistance.

◆ Characteristics : Reinforced PA6 material features excellent molded surface quality, thermal stability, hydrolysis resistance and alcoholysis resistance.

◆ Purpose : Automotive parts, mechanical components and electronic and electrical fields.

◆ Benchmark Against : SIRMAX A 6 GF30 HSR

Technical Parameters
项 目
Item		 数 值
Value		 单 位
Unit		 测试标准
Standard		 测试条件
Condition
Density 1.37 g/cm3 ISO 1183 23℃/55%RH
Filler Contents 30 % ISO 3451 800℃/2H
Tensile Strength 180 Mpa ISO 527-2 5mm/min
Elongation at Break 3.5 % ISO 527-2 5mm/min
Tensile Modulus 9500 Mpa ISO 527-2 5mm/min
Flexural Strength 255 Mpa ISO 178 2mm/min
Flexural Modulus 7800 Mpa ISO 178 2mm/min
Charpy impact strength 18 KJ/ M2 ISO 180/1A 2.75J
Charpy Unnotched impact strength 83 KJ/ M2 ISO 180/1U 5.5J
Flammability HB class UL-94 -
Melt Point 220 ℃ ISO 11357 -

* If you need the material PA6 GF30 HSLR or require customized production with special specifications, you can contact us at email sales@anixt.com ,We will reply promptly!

Previous : PA6 GF60 HSL

Next : PA6 B3ZG3