PA6 Modification

Raw Materials Modified Nylon

PA6 B3WG12 HSP

Home > Products > Modified Nylon > PA6 Modification
Brand : Anixt® PA6 B3WG12 HSP
Labels : PA6 (Polyamide 6) reinforced with 60% glass fiber, heat-stabilized and high-flow material.
Tags: PA6B3WG12HSP BASFB3WG12HSP PA6GF60HSL LANXESSBKV60H2.0EF
InquiryInquiry
  • PA6 B3WG12 HSP
Product Description
Overview

◆ Material : PA6 (Polyamide 6) reinforced with 60% glass fiber, heat-stabilized and high-flow material.

◆ Characteristics : Glass fibre reinforced and heat ageing resistant injection moulding grade with high flowability and excellent surface quality for structural parts with very high stiffness requirements.

◆ Purpose : Automotive: engine compartment structural parts, intake manifolds, seat frames, transmission components, battery brackets. Electrical and Electronic: high-voltage electrical housings, terminal blocks, connector frames, power module cooling brackets. Industrial Machinery: high-strength gears, bearing housings, pump casings, structural supports.

◆ Benchmark Against : BASF B3WG12 HSP,PA6 GF60 HSL,LANXESS BKV60H2.0EF

Technical Parameters
项 目
Item		 数 值
Value		 单 位
Unit		 测试标准
Standard		 测试条件
Condition
Density 1.72 g/cm3 ISO 1183 23℃/55%RH
Filler Contents 60 % ISO 3451 800℃/2H
Tensile Strength 250 Mpa ISO 527-2 5mm/min
Elongation at Break 2.5 % ISO 527-2 5mm/min
Tensile Modulus 21500 Mpa ISO 527-2 5mm/min
Flexural Strength 300 Mpa ISO 178 2mm/min
Flexural Modulus 20000 Mpa ISO 178 2mm/min
Charpy impact strength 16 KJ/ M2 ISO 180/1A 2.75J
Charpy Unnotched impact strength 95 KJ/ M2 ISO 180/1U 5.5J
Flammability HB class UL-94 -
Melt Point 220 ℃ ISO 11357 -

* If you need the material PA6 B3WG12 HSP or require customized production with special specifications, you can contact us at email sales@anixt.com ,We will reply promptly!

Previous : PA6 GF50 HSL

Next : PA6 DP-BKV60H2.0EF