Labels : High barrier property, high modulus, good heat resistance, low water absorption.
InquiryInquiry
  • Self-adhesive Tie Mounts 1-1
Product Description
Overview

◆ PAMXD6 L02 Material : High barrier property, high modulus, good heat resistance, low water absorption.

◆ PAMXD6 L02 Characteristics : High strength, strong rigidity, high heat resistance, and low water absorption.

◆ PAMXD6 L02 Purpose : Electronic precision components, optical structures, camera mounts.

◆ PAMXD6 L02 Benchmark Against : American Solvay,Mitsubishi

Technical Parameters
项 目
Item		 测试标准
Standard		 测试条件
Condition		 单 位
Unit		 数 值
Value
Density ISO 1183 23℃/55%RH g/cm3 1.22
Filler Contents ISO 3451 800℃/2H % -
Tensile Strength ISO 527-2 5mm/min Mpa 99
Elongation at Break ISO 527-2 5mm/min % 2.3
Tensile Modulus ISO 527-2 5mm/min Mpa 4700
Flexural Strength ISO 178 2mm/min Mpa 160
Flexural Modulus ISO 178 2mm/min Mpa 4400
Izod Notched Impact Strength ISO 180/1A 2.75J KJ/ M2 3.5
Izod Unnotched Impact Strength ISO 180/1U 5.5J KJ/ M2 N
Flammability UL-94 - class HB
Melt Point ISO 11357 - ℃ 240