◆ Material : PA66 GF25 HSL is a 25% glass fiber reinforced, heat-stabilized, internally lubricated PA66 grade.
◆ Characteristics : High strength and rigidity from 25% glass fiber. Excellent long-term heat aging performance. Good dimensional stability and low warpage. Internal lubricant improves processability and surface quality. Good resistance to oils, fuels and common chemicals.
◆ Purpose : Automotive: engine compartment parts, housings, brackets, gear components, fan parts. Electrical & electronic: connectors, bobbins, relay bases, circuit breakers. Industrial: power tool parts, pump components, mechanical structural parts.
◆ Benchmark Against : DUPONT 70G25HSL,BASF A3WG5
| 项 目 Item |
数 值 Value |
单 位 Unit |
测试标准 Standard |
测试条件 Condition |
| Density | 1.33 | g/cm3 | ISO 1183 | 23℃/55%RH |
| Filler Contents | 25 | % | ISO 3451 | 800℃/2H |
| Tensile Strength | 170 | Mpa | ISO 527-2 | 5mm/min |
| Elongation at Break | 3.0 | % | ISO 527-2 | 5mm/min |
| Tensile Modulus | 9000 | Mpa | ISO 527-2 | 5mm/min |
| Flexural Strength | 230 | Mpa | ISO 178 | 2mm/min |
| Flexural Modulus | 6500 | Mpa | ISO 178 | 2mm/min |
| Charpy impact strength | 9 | KJ/ M2 | ISO 180/1A | 2.75J |
| Charpy Unnotched impact strength | 50 | KJ/ M2 | ISO 180/1U | 5.5J |
| Flammability | HB | class | UL-94 | - |
| Melt Point | 260 | ℃ | ISO 11357 | - |