PA66 Modification

Raw Materials Modified Nylon

PA66 GF30 MS

Home > Products > Modified Nylon > PA66 Modification
Brand : Anixt® PA66 GF30 MS
Labels : PA66 wear-resistant modified reinforcement material (molybdenum disulfide) has excellent wear resistance and good mechanical properties.
Tags: PA66GF30MS PA205MS RTP205MS
InquiryInquiry
  • PA66 GF30 MS
Product Description
Overview

◆ Material : PA66 wear-resistant modified reinforcement material (molybdenum disulfide) has excellent wear resistance and good mechanical properties.

◆ Characteristics : PA66+30% fiberglass reinforcement, MoS2 wear-resistant modification, low wear, high rigidity.

◆ Purpose : Machinery: transmission components, sliders, guide rails, wear-resistant gears. Automobile: engine peripherals, gears, bearing seats, wear-resistant structural components. Electronic and electrical: high-strength wear-resistant shell, structural components.

◆ Benchmark Against : RTP 205 MS,PA66 GF30 MS

Technical Parameters
项 目
Item		 数 值
Value		 单 位
Unit		 测试标准
Standard		 测试条件
Condition
Density 1.40 g/cm3 ISO 1183 23℃/55%RH
Filler Contents 30 % ISO 3451 800℃/2H
Tensile Strength 175 Mpa ISO 527-2 5mm/min
Elongation at Break 3.2 % ISO 527-2 5mm/min
Tensile Modulus 10500 Mpa ISO 527-2 5mm/min
Flexural Strength 250 Mpa ISO 178 2mm/min
Flexural Modulus 7800 Mpa ISO 178 2mm/min
Charpy impact strength 12 KJ/ M2 ISO 180/1A 2.75J
Charpy Unnotched impact strength 77 KJ/ M2 ISO 180/1U 5.5J
Flammability HB class UL-94 -
Melt Point 260 ℃ ISO 11357 -

* If you need the material PA66 GF30 MS or require customized production with special specifications, you can contact us at email sales@anixt.com ,We will reply promptly!

Previous : PA 205 MS

Next : PA66 PTFE5