◆ Material : 30% Glass Reinforced, Heat Stabilized, Flame Retardant, High Flow
◆ Characteristics : Characteristic highlights: high flow, thermal stability, suitable for thin-walled structural parts (significantly better filling ability compared to ordinary PA6-GF30 FR)
◆ Purpose : Specializing in thin-walled complex electrical components, including new energy charging guns/charging plugs, connectors, switches, relay housings, and thin-walled structural components for small circuit breakers; The flowability is better than that of conventional flame retardant PA6-GF30.
◆ Benchmark Against : DSM K-FKGS6/B,RTP 205 A FR,Durethan BKV30N1000000
| 项 目 Item |
数 值 Value |
单 位 Unit |
测试标准 Standard |
测试条件 Condition |
| Density | 1.55 | g/cm3 | ISO 1183 | 23℃/55%RH |
| Filler Contents | 30 | % | ISO 3451 | 800℃/2H |
| Tensile Strength | 160 | Mpa | ISO 527-2 | 5mm/min |
| Elongation at Break | 2.3 | % | ISO 527-2 | 5mm/min |
| Tensile Modulus | 12500 | Mpa | ISO 527-2 | 5mm/min |
| Flexural Strength | 245 | Mpa | ISO 178 | 2mm/min |
| Flexural Modulus | 10800 | Mpa | ISO 178 | 2mm/min |
| Charpy impact strength | 12 | KJ/ M2 | ISO 180/1A | 2.75J |
| Charpy Unnotched impact strength | 55 | KJ/ M2 | ISO 180/1U | 5.5J |
| Flammability | V0 | class | UL-94 | - |
| Melt Point | 220 | ℃ | ISO 11357 | - |
* If you need the material PA6 K-FKGS6 or require customized production with special specifications, you can contact us at email sales@anixt.com ,We will reply promptly!